Features of the synthesis of calcium-aluminate phases with the introduction of modifying additives
Tác giả: Mikhail Alexandrovich Trubitsyn, L.V. Furda, N.A. Volovicheva, M.N. Yapryntsev, Le Van Thuan
Số trang:
P. 61-68
Tên tạp chí:
Khoa học & Công nghệ Đại học Duy Tân
Số phát hành:
P. 61-68
Kiểu tài liệu:
Tạp chí trong nước
Nơi lưu trữ:
03 Quang Trung
Mã phân loại:
540
Ngôn ngữ:
Tiếng Anh
Từ khóa:
Calcium-aluminate phases, heat treatment, boric acid, high alumina cement, modification
Chủ đề:
Chemistry
Tóm tắt:
In this work, the influences of boric acid and high alumina cement used as modifying additives on the formation of CaO∙Al2O3 and CaO∙2Al2O3 were studied. Herein, commercially available chalk of the M-90 label and technical alumina of the G-0 label were utilized as initial raw materials. Heat treatment of powder mixtures with various concentrations of modifying additives was carried out in the temperature range of 1250-1350oC with an isothermal exposure times of 1h and 2h. It was found that the addition of additives into the raw mixture affected the ratio of target phases and the temperature interval of the phase formation of calcium-aluminate minerals.
Tạp chí liên quan
- Thực trạng hoạt động quản lý chất lượng dịch vụ khám bệnh, chữa bệnh ở các bệnh viện đa khoa công lập hạng II tại thành phố Hà Nội năm 2024
- Đánh giá tác động của đột biển gen IDH1 và sự methyl hóa gen MGMT đến thời gian sống thêm toàn bộ trên bệnh nhân u nguyên bào thần kinh đệm
- Xác định đột biến gen EIF4G1 trên bệnh nhân Parkinson
- Tỷ lệ hiện mắc, các yếu tố nguy cơ và kết quả điều trị tổn thương thận cấp tại Khoa Hồi sức tích cực, Bệnh viện Đa khoa tỉnh Vĩnh Phúc
- Chuyển đổi số, khả năng vượt các rào cản xuất khẩu và tác động đến kết quả xuất khẩu của doanh nghiệp