Fabrication of Cu2ZnSn(SxSe1-x)4 thin film solar cell using spray pyrolysis method = Chế tạo pin mặt trời màng mỏng Cu2ZnSn(SxSe1-x)4 bằng phương pháp phun nóng
Tác giả: Nguyen Thi Hiep, Tran Nguyen Tien, Ung Thi Dieu Thuy
Số trang:
P. 58-63
Số phát hành:
Số 05 (60) - Tháng 10
Kiểu tài liệu:
Tạp chí trong nước
Nơi lưu trữ:
03 Quang Trung
Mã phân loại:
621
Ngôn ngữ:
Tiếng Anh
Từ khóa:
Cu2ZnSn(SxSe1-x)4, thin-film solar cells, spray pyrolysis method
Chủ đề:
Electronics--Materials
Tóm tắt:
A kesterite Cu2ZnSn(SxSe1-x)4 (CZTSSe) thin film is fabricated on a Mo-coated glass substrate by a non-vacuum spray pyrolysis method from an aqueous precursor solution containing Cu(NO3)2, Zn(NO3)2, Sn(CH3SO3)2 and thiourea followed by sulfurization and selenization at 600°C. The fabricated CZTSSe thin film shows high crystallinity with optimal Cu-poor and Zn-rich compositions, which is confirmed by the X-ray diffraction pattern, Raman spectrum, and Energy dispersive X-ray spectroscopy results.
Tạp chí liên quan
- Ảnh hưởng của thành phần chất nền, nồng độ tạp và công nghệ chế tạo lên tính chất nhiệt phát quang của liều kế thủy tinh Li2B4O7:Tm
- Ảnh hưởng của tỉ lệ Na/Al đến tính chất quang của ion Eu3+ trong thủy tinh x.Na2O-(25-x).Al2O3-75SiO2-0.5Eu2O3
- Đường cong nóng chảy của kim loại crôm ở áp suất cao
- Trạng thái ngưng tụ exciton mất cân bằng khối lượng trong bán kim loại/ bán dẫn
- Đặc điểm hình thái, giải phẫu và định lượng axít corosolic trong lá Bằng lăng ổi (Lagerstroemia calyculata Kurz) tại vùng Đông Nam Bộ, Việt Nam