Features of the synthesis of calcium-aluminate phases with the introduction of modifying additives
Tác giả: Mikhail Alexandrovich Trubitsyn, L.V. Furda, N.A. Volovicheva, M.N. Yapryntsev, Le Van Thuan
Số trang:
P. 61-68
Tên tạp chí:
Khoa học & Công nghệ Đại học Duy Tân
Số phát hành:
P. 61-68
Kiểu tài liệu:
Tạp chí trong nước
Nơi lưu trữ:
03 Quang Trung
Mã phân loại:
540
Ngôn ngữ:
Tiếng Anh
Từ khóa:
Calcium-aluminate phases, heat treatment, boric acid, high alumina cement, modification
Chủ đề:
Chemistry
Tóm tắt:
In this work, the influences of boric acid and high alumina cement used as modifying additives on the formation of CaO∙Al2O3 and CaO∙2Al2O3 were studied. Herein, commercially available chalk of the M-90 label and technical alumina of the G-0 label were utilized as initial raw materials. Heat treatment of powder mixtures with various concentrations of modifying additives was carried out in the temperature range of 1250-1350oC with an isothermal exposure times of 1h and 2h. It was found that the addition of additives into the raw mixture affected the ratio of target phases and the temperature interval of the phase formation of calcium-aluminate minerals.
Tạp chí liên quan
- Tổng quan về ứng dụng nano oxit kim loại trong xúc tác quang hóa phân hủy các phẩm màu nhuộm
- Nghiên cứu ảnh hưởng của hiệu ứng đồng vị đến hệ số Debye-Waller của các tinh thể khí hiếm
- Existence results and numerical solution of fully fourth order nonlinear functional differential equations
- Hydrogen trong cân bằng năng lượng toàn cầu
- Giải pháp nâng cao hiệu quả sử dụng vốn lưu động tại Công ty TNHH Tuấn Khanh Thái Nguyên